Observations on the distribution of sulfur nanoparticles on suspended and supported graphene layers
编号：237 访问权限：PARTICIPANT_ONLY 更新：2022-09-27 17:05:35 浏览：1206次 口头报告

报告开始：2023-04-23 15:10

报告时间：15min

所在会场：[N] 摩擦学表面工程论坛二 [N2] 下午场

暂无文件

摘要
In this paper, we report the distinct difference in the distributions of sulfur nanoparticles(NPs) on suspended graphene compared to supported one. With vapor deposition of sulfur NPs onto graphene with patterned substrate, we find that the density of NPs on supported regions is 3 to 8 times larger than that on suspended ones. Different correlations between density and number of graphene layers are observed, being positive for suspended and negative for supported regions. The density also increases with the area of the suspended regions. The mechanism underlying these phenomena is attributed to the ripple induced enhanced diffusion of sulfur on suspended graphene.

 
关键词
Nanoparticle, Suspended Graphene, Diffusion, Vapor Deposition
报告人
何雨勍
清华大学机械系

发表评论
验证码 看不清楚，更换一张
全部评论
重要日期

  • 会议日期

    04-21

    2023

    至

    04-23

    2023

  • 04-20 2023

    Draft paper submission deadline

  • 04-23 2023

    Registration deadline

主办单位

中国机械工程学会表面工程分会

承办单位

武汉材料保护研究所有限公司
特种表面保护材料及应用技术国家重点实验室

联系方式
历届会议

表面工程在线是由中国机械总院集团武汉材料保护研究所有限公司组建的一个面向我国表面工程行业的服务性平台，平台得到了中国机械工程学会表面工程分会、中国机械工程学会摩擦学分会、中国腐蚀与防护学会以及国内众多科研院所和高校等组织机构的大力支持。平台有能力整合多方资源，愿为我国表面工程行业的蓬勃发展贡献力量！